Abstract The effect of temperature was investigated on the consolidation of blended elemental powders of aluminum and copper by equal channel angular pressing (ECAP). Aluminum and Copper powders (1:1% vol.) were blended and consolidated in a 90° ECAP die at room (RT) and cryogenic temperatures (CT - ~77 K). ECAP samples were pressed until 4 passes at room temperature in route Bc. As a reference, a sample was obtained by conventional uniaxial pressing. The obtained results indicated a much denser (>99.5%) and harder structure by cryogenic ECAP. The hardness after one pass at CT was comparable with 4 passes at room temperature. Tensile tests performed at CT for materials with similar chemical composition showed a simultaneous increase in strength and ductility at CT, corroborating the results obtained by ECAP. The partial suppression of dynamic recovery and the activation and the transition between deformation mechanisms at CT, as well as stacking fault energies (SFE) of such metals, played an important role in these results. Copper presented a much higher capability of strain hardening than aluminum, due to its lower SFE and much lower homologous temperature. X-ray diffraction indicated a strong correlation between the variation of average microstrain and the variation of hardness on both metals. The results of this study demonstrated the great potential of the application of very low temperatures for the obtaining of deformation metal-metal composites.

Equal channel angular pressing (ECAP) is one of the severe plastic deformation processes that can also be used for metallic powder consolidation. Consolidation of blended elemental powders of iron, chromium, nickel, and manganese (Fe-25Cr-20Ni-2Mn wt. %) was performed at room temperature in a Φ = 120° die by 1 and 2 passes. SEM micrographs indicated that single pass ECAP consolidated sample presented close to full densification. Additional pass of ECAP led to hardness increase and to an apparent better mixing between the different particles. SEM/EDX analysis made before and after heat treatment of the samples showed that effective diffusion only took place after heat treatment and especially in the sample subjected to 2 ECAP passes. Results indicate that alloying by ECAP consolidation and posterior heat treatment is feasible, especially for systems that cannot be processed by conventional means, as well as mechanical alloying.

A [211]-oriented niobium single crystal was deformed by equal channel angular pressing (ECAP) at room temperature using the route Bc to a total strain of 9.2. A sharp cube texture develops after ECAP processing. The deformed samples were annealed in vacuum from 400ºC (673 K) to 900ºC (1173 K) for 1 h to evaluate their microstructural stability. Scanning electron microscopy (SEM) was used to image the microstructures of as-deformed and annealed specimens. Electron backscatter diffraction (EBSD) was employed to determine the respective microtextures before and after annealing. Coarsening of the microstructure occurs at a maximum rate at 550ºC (823 K) due to discontinuous recrystallization. Normal grain growth replaces discontinuous recrystallization as the main coarsening mechanism above 700ºC (973 K).